Effects of Prior Aging at 288 C in Argon Environment on Creep Response of Carbon Fiber Reinforced Pmr-15 Composite with 45 Fiber Orientation at 288 C - Prijzen

The creep and recovery response of carbon fiber reinforced PMR-15 composite with a 45 fiber orientation was examined in an argon environment at 288 C. Mechanical testing was executed for unaged specimens as well as specimens aged up to 1000 hours. Tensile tests were performed to determine Young's modulus of elasticity and ultimate tensile strength. The creep tests were carried out at stress levels of 30 and 60 MPa. Creep periods of 25 hours were...

De Effects of Prior Aging at 288 C in Argon Environment on Creep Response of Carbon Fiber Reinforced Pmr-15 Composite with 45 Fiber Orientation at 288 C is een populaire optie voor Onderwijs & Didactiek. Esy heeft 1 prijs gevonden, de goedkoopste keuze is volgens ons Bol, maar bekijk de andere aanbieders om het zeker te weten. Links openen in een nieuwe tabblad. Bekijk hier onder de product specificaties. Meer product informatie beschikbaar bij Bol.

Productspecificaties

Waar te koop

Effects of Prior Aging at 288 C in Argon Environment on Creep Response of Carbon Fiber Reinforced Pmr-15 Composite with 45 Fiber Orientation at 288 C is onder andere te koop bij: Bol. Esy raadt altijd aan om meerdere aanbieders te bekijken om geen last minute deals mis te lopen.